20 # steel pipe material is 20 steel, generally 20 seamless steel pipe 20 # steel pipe material is: high-quality carbon structural steel brand: 20 steel standard: GB/T 699-1999 & GB/T 3639-2008
â—Characteristics and application scope:
Cold deformation high plasticity, general for bending, rolling, crimping and hammer arch processing, arc welding and contact welding welding performance, gas welding thickness is small, strict shape or complex shape of the parts are prone to cracks. Machinability Cold drawing or normalizing is better than annealing. It is generally used for manufacturing with low stress and high toughness requirements.
â— Chemical composition:
Carbon C: 0.17 to 0.23 Silicon Si: 0.17 to 0.37 Manganese Mn: 0.35 to 0.65 Sulfur S: ≤ 0.035 Phosphorus P: ≤ 0.035 Chromium Cr: 0.25 Nickel Ni: 0.25 Copper Cu: 0.25
â—Mechanical properties:
Tensile strength σb (MPa): ≥410 (42) Yield strength σs (MPa): ≥ 245 (25) Elongation δ5 (%): ≥25 Section shrinkage ψ (%): ≥ 5, Hardness: Not treated , ≤156HB, sample size: sample size 25mm
â— Heat Treatment Specification and Metallographic Organization:
Heat treatment specifications: normalizing, 910°C, air cooling. Metallographic structure: ferrite + pearlite.
â—Delivery status: Delivery with no heat treatment or heat treatment (annealing, normalizing or high temperature tempering). The requirements for the delivery of heat treatment shall be specified in the contract, and those not specified shall be delivered without heat treatment.
20 # steel weight formula: [(outer diameter - wall thickness) * wall thickness] * 0.02466 = kg / meter (weight per meter)
Steel pipe weight formula For example: [(68-4)*4]*0.02466*1=6.31296 (kg/m)
This pipe knowledge is provided by.
â—Characteristics and application scope:
Cold deformation high plasticity, general for bending, rolling, crimping and hammer arch processing, arc welding and contact welding welding performance, gas welding thickness is small, strict shape or complex shape of the parts are prone to cracks. Machinability Cold drawing or normalizing is better than annealing. It is generally used for manufacturing with low stress and high toughness requirements.
â— Chemical composition:
Carbon C: 0.17 to 0.23 Silicon Si: 0.17 to 0.37 Manganese Mn: 0.35 to 0.65 Sulfur S: ≤ 0.035 Phosphorus P: ≤ 0.035 Chromium Cr: 0.25 Nickel Ni: 0.25 Copper Cu: 0.25
â—Mechanical properties:
Tensile strength σb (MPa): ≥410 (42) Yield strength σs (MPa): ≥ 245 (25) Elongation δ5 (%): ≥25 Section shrinkage ψ (%): ≥ 5, Hardness: Not treated , ≤156HB, sample size: sample size 25mm
â— Heat Treatment Specification and Metallographic Organization:
Heat treatment specifications: normalizing, 910°C, air cooling. Metallographic structure: ferrite + pearlite.
â—Delivery status: Delivery with no heat treatment or heat treatment (annealing, normalizing or high temperature tempering). The requirements for the delivery of heat treatment shall be specified in the contract, and those not specified shall be delivered without heat treatment.
20 # steel weight formula: [(outer diameter - wall thickness) * wall thickness] * 0.02466 = kg / meter (weight per meter)
Steel pipe weight formula For example: [(68-4)*4]*0.02466*1=6.31296 (kg/m)
This pipe knowledge is provided by.
â— Depth control can adjust the nails depth.
â— Designed with 2-in-1 magazine applicabel for both brads and nails.
â— Quick clear nose for removing nail jams.
â— Easy Insurance design, to use safe, secure.
â— Easy-molded rubber handle and ergonomic gun body design operation.
◠Heavy-Duty Steel Cap,360° exhaust cover and exhaust air away from users.
2 In 1 Combination Tools,2 In 1 Combination Tools Set,2 In 1 Combination Hand Tools,Useful 2 In 1 Combination Tools,2-In-1 Comb Nailer / Stapler
DAHOO Tools Co., Ltd. , http://www.dahootools.com