1060 is formed by adding a small amount of copper element to pure aluminum, which has excellent forming processing characteristics, high corrosion resistance, good weldability and electrical conductivity. Widely used in products with low requirements on strength, such as chemical equipment, sheet metal processing parts, deep drawing or spinning concave vessels, welding parts, heat exchangers, clock surfaces and plates, nameplates, kitchen utensils, decorations, reflectors, etc. . Chemical Composition Limits wt% Cu Si Fe Mn Mg Zn Cr Ti Pb.Bi Al 0.05 0.25 0.35 0.03 0.03 0.05 / 0.03 / >99.60 Typical Alloy 1060-H14 Mechanical and Physical Properties (Typical Mechanical & Physical Properties) Weldability Machinability Corrosion resistance Conductivity 20°C (68?) (%IACS) density (20°C)(g/cm3) well not good well 55-63 2.70 tensile strength (25°C MPa) Yield Strength (25°C MPa) hardness 500kg force 10mm ball Elongation rate 1.6mm (1/16in) thickness Large shear stress MPa 100 90 26 12 55